Research into materials that have high efficiencies of thermoelectric heat-energy conversion has been at a plateau since the middle of the last century. During this time, efficiencies have been engineered high enough for several interesting niche applications but not high enough for widespread adaptation into traditional power generation or refrigeration technologies. The past decade has seen considerable advancement, as a number of theoretical works have suggested that lower dimensional structures could hold the key for enhanced efficiency, and several experiments have provided the proof of principle needed to inspire just such a research direction. The benefit of low dimensional structures for thermoelectric efficiency comes from both the potential enhancement of the electronic properties due to quantum confinement effects as well as from the potential for increased scattering of heat-carrying phonons. Widespread application of these principles for technological application requires the creation of composites of nanostructures that can be manufactured easily with dimensions on the bulk materials scale. A good starting point for such materials research is to manufacture composites of materials that are currently known to have high thermoelectric efficiencies by incorporating nanostructures into a bulk matrix.
The goal of this project is to create nanocomposites using bismuth telluride, a compound known to have one of the highest thermoelectric efficiencies at room temperature, as a matrix material. Various methods of synthesizing sufficient quantities of bismuth telluride nanostructures were attempted, including pulsed laser vaporization, chemical vapor deposition, and solvothermal synthesis. The method of solvothermal synthesis was found to be the simplest approach for producing high yields of bismuth telluride nanostructures. In the initial stages of the project, cold pressing was tested as a means of compaction, but in the end a uniaxial hot pressing technique was adopted in order to consolidate the nanostructures into the bulk matrix.
Nanocomposites were produced using both n-type and p-type bismuth telluride compounds as the matrix material, into which nanostructures of Bi2Te 3, BiSb, Bi2S3, as well as Au and Ag nanoparticles and C60 were incorporated. The preferred consolidation technique utilized a 3-axis mechanical mixer, followed first by cold and then hot pressing of the bulk-nano mixtures. The composites were studied with respect to their microstructure and elemental composition, as well as with regard to their thermal and electrical transport properties. The effects of the nanoparticle additions upon the efficiencies of the materials are presented, and the viability of improving the thermoelectric performance of this class of materials by this method is considered.
|Advisor:||Tritt, Terry M.|
|Commitee:||Marinescu, Catalina D., Rao, Apparao M., Sosolik, Chad E.|
|School Location:||United States -- South Carolina|
|Source:||DAI-B 69/07, Dissertation Abstracts International|
|Keywords:||Bismuth telluride, Nanoparticle inclusions, Thermoelectric transport|
Copyright in each Dissertation and Thesis is retained by the author. All Rights Reserved
The supplemental file or files you are about to download were provided to ProQuest by the author as part of a
dissertation or thesis. The supplemental files are provided "AS IS" without warranty. ProQuest is not responsible for the
content, format or impact on the supplemental file(s) on our system. in some cases, the file type may be unknown or
may be a .exe file. We recommend caution as you open such files.
Copyright of the original materials contained in the supplemental file is retained by the author and your access to the
supplemental files is subject to the ProQuest Terms and Conditions of use.
Depending on the size of the file(s) you are downloading, the system may take some time to download them. Please be