The fabrication of highly charged and highly durable proton-exchange membranes (PEMs) is a critical step toward improving the performance and lifetime of hydrogen fuel cells. State of the art commercial PEMs from perfluorosulfonic acid ionomers suffer from excessive swelling when exposed to water. The present work’s objective was to investigate the use of electrospinning for the fabrication of highly charged (highly proton conductive) composite PEMs with low in-plane swelling. A series of membranes consisting of a low equivalent weight (i.e. highly charged) ionomer and an uncharged reinforcing polymer were prepared using dual fiber electrospinning (where ionomer and uncharged polymer are separately electrospun) and single fiber electrospinning (where ionomer and uncharged polymer are electrospun from a common solution). For the dual fiber membranes, the distribution of the uncharged reinforcing polymer in the thickness direction was varied (leading to a multi-layered membrane) or the average diameter of the reinforcing polymer was varied. For both the single fiber and dual fiber membranes, ionomers of varying equivalent weights were Incorporated into films with the same effective concentration of fixed charge groups. The dependence of membrane structure, ionomer equivalent weight and side chain chemistry on membrane conductivity and swelling was investigated, and the relevance of the results to fuel cell performance was discussed. The addition of a small amount of uncharged reinforcing polymer in an electrospun membrane led to a significant reduction in swelling, while conductivity generally followed a simple ionomer weight fraction mixing rule. Dual fiber membranes exhibited the best combination of properties, achieving low in-plane water swelling (as low as 4%) with high conductivities (up to 0.1 S/cm in 25°C water).
|Advisor:||Pintauro, Peter N.|
|Commitee:||Guelcher, Scott, Laibinis, Paul E., Lin, Shihong|
|Department:||Chemical and Biomolecular Engineering|
|School Location:||United States -- Tennessee|
|Source:||DAI-B 81/3(E), Dissertation Abstracts International|
|Subjects:||Alternative Energy, Chemical engineering|
|Keywords:||Electrospinning, Membrane, Polymer, Structure|
Copyright in each Dissertation and Thesis is retained by the author. All Rights Reserved
The supplemental file or files you are about to download were provided to ProQuest by the author as part of a
dissertation or thesis. The supplemental files are provided "AS IS" without warranty. ProQuest is not responsible for the
content, format or impact on the supplemental file(s) on our system. in some cases, the file type may be unknown or
may be a .exe file. We recommend caution as you open such files.
Copyright of the original materials contained in the supplemental file is retained by the author and your access to the
supplemental files is subject to the ProQuest Terms and Conditions of use.
Depending on the size of the file(s) you are downloading, the system may take some time to download them. Please be