Aluminum alloys have increasing applications in construction and transportation industries. Both 5xxx-series (Al-Mg) and 6xxx-series (Al-Mg) alloys are frequently used in marine construction because of their light weight, high strength, and corrosion resistance. One of the major concerns regarding the marine application of aluminum alloys is their mechanical performance in fire scenarios. The material strength may be degraded due to both thermal and mechanical damage during fire exposure.
This work emphasizes the stress-induced mechanical (physical) damage and its impact on the residual (post-fire) performance of 5083-H116 and 6061-T651 aluminum alloy. Thermomechanical tests were performed at various temperatures and stresses to study the stress-induced damage at induced plastic creep strain levels. Unstressed thermally exposed and thermomechanically damaged samples were examined to separate the stress-induced microstructural damage. The stress-induced microstructural damage primarily manifests itself as dynamic recovery at low creep temperatures, while cavitation, dynamic recrystallization and dynamic precipitation (in Al6061) are the types of damage developed in the high creep strains at high exposure temperatures. Different creep mechanisms are also studied for both Al5083 and Al6061.
The post-fire mechanical response at room temperature after thermo-mechanical damage was investigated with reference to the damaged microstructure present in the material. Residual material strengths based on deformed cross sectional area after the creep test were calculated to provide insight into how microstructural damage affects the post-fire material performance. The competing effects of strength degradation caused by cavitation and strengthening due to grain elongation and subgrain refinement were investigated. Engineering residual material strengths calculated based on the original cross sectional area prior to creep tests were also studied to provide guidance for structural design.
|Advisor:||Case, Scott W.|
|School:||Virginia Polytechnic Institute and State University|
|School Location:||United States -- Virginia|
|Source:||DAI-B 78/09(E), Dissertation Abstracts International|
|Subjects:||Mechanics, Mechanical engineering, Materials science|
|Keywords:||Aluminum alloys, Cavitation, Fire response, Grain deformation, Residual strength, Stress-induced damage|
Copyright in each Dissertation and Thesis is retained by the author. All Rights Reserved
The supplemental file or files you are about to download were provided to ProQuest by the author as part of a
dissertation or thesis. The supplemental files are provided "AS IS" without warranty. ProQuest is not responsible for the
content, format or impact on the supplemental file(s) on our system. in some cases, the file type may be unknown or
may be a .exe file. We recommend caution as you open such files.
Copyright of the original materials contained in the supplemental file is retained by the author and your access to the
supplemental files is subject to the ProQuest Terms and Conditions of use.
Depending on the size of the file(s) you are downloading, the system may take some time to download them. Please be