The responses of structure and properties to composition and temperature have been investigated for glasses in TiO2-SiO2 and Na2O-TiO2-SiO2 systems. Additionally, the response of Na2O-TiO2-SiO2 glasses to plastic deformation has been studied. (x)TiO2-(1-x)SiO2 glasses were prepared through the sol-gel process with compositions 0 ≤ x ≤ 10 mol% and compared to commercial glasses prepared through flame hydrolysis deposition with x = 0, 5.4, and 8.3 mol%. (x) Na2O - (y) TiO 2 - (1-x-y) SiO2 glasses were prepared with x = 10, 15, 20, and 25 mol% and y = 4, 7, and 10 mol% through a melt-quench process. Density and index of refraction of glasses was measured through the Archimedes's method and using a prism coupler, respectively. The glass transition temperature of Na2O-TiO2-SiO2 glasses was measured through differential thermal analysis.
The structure and elastic moduli have been studied through Raman spectroscopy and Brillouin light scattering, respectively, at room temperature and in-situ up to 1200 °C for TiO2-SiO2 glasses and up to 800 °C for Na2O-TiO2-SiO2 glasses. Young's modulus was observed to decrease from 72 GPa to 66 GPa with the addition of 8.3 mol% TiO2 in TiO2-SiO2 glasses and to increase from 65 GPa to 73 GPa with the addition of 10 mol% TiO2 in 10 Na2O - (0-10) TiO2-SiO2 glasses. The addition of TiO2 was observed to shift the 460, 490, and 600 cm-1 Raman peaks to lower frequencies in TiO2-SiO2 glasses, suggesting a more open and flexible network, and the 720, 800, and 840 cm -1 Raman peaks to higher frequencies in Na2O-TiO2 -SiO2 glasses, suggesting a lower free volume and stiffer network. The addition of TiO2 has little effect on the temperature response of the elastic moduli in either system, but decreases the thermal expansion and increases the frequency shifts in the 950 and 1100 cm -1 Raman peaks in the TiO2-SiO2 system while the thermal expansion increases with initial additions of TiO2 and then remains constant in the Na2O-TiO2-SiO 2 system.
Changes in structure and property with composition have been discussed, and structural models were proposed. The reduction of thermal expansion and elastic moduli in TiO2-SiO2 glasses occurs through the promotion of cooperative, inter-tetrahedral rotations facilitated by the longer and weaker Ti-O bonds. The increase in elastic moduli in the Na2O-TiO 2-SiO2 glasses occurs through the formation of small clusters with local, relatively high Ti and Na concentrations, promoted by Ti adopting a five-fold coordination in a square-pyramidal geometry. These clusters work to shield the silica network from non-bridging oxygens from the presence of Na while simultaneously increasing the volume bond density of the glass.
For Na2O-TiO2-SiO2 glasses, the response to mechanical damage and plastic deformation has been examined through Vickers indentation experiments at loads from 10 mN to 49 N. Fracture toughness was measured through the single-edge precracked beam method. The permanent deformation volumes around Vickers indents were investigated through atomic force microscopy. Critical loads for crack initiation and cracking patterns were systematically investigated and correlated with the elastic properties of glass. Vickers indents were observed to change from a mixture of radial/median and cone cracks to radial/median and lateral cracks as Poisson's ratio increases. As Poisson's ratio increases hardness decreases from 5.5 GPa to 4.5 GPa, the average radial/median crack length roughly doubles, and fracture toughness remains constant. A minimum in the critical crack initiation load was observed at ν = 0.21–0.22. The volume of glass deformed through shear flow during indentation increases gradually with increasing Poisson's ratio, becomes larger than the densified volume at ν = 0.237. The densified volume increases between ν = 0.18 and ν = 0.21 and decreases rapidly from 16.5 µm3 to 8.7 µm3 at ν = 0.235–0.237. A correlation between the minimum in crack initiation load and the change in deformation mechanisms over the same Poisson’s ratio range was observed.
|Advisor:||Huang, Liping, Rouxel, Tanguy|
|Commitee:||Davis, Mark, Glaesemann, Scott, Gross, Timothy, Tomozawa, Minoru, Watson, E. Bruce, Wondraczek, Lothar|
|School:||Rensselaer Polytechnic Institute|
|School Location:||United States -- New York|
|Source:||DAI-B 78/01(E), Dissertation Abstracts International|
|Keywords:||Brillouin spectroscopy, Deformation mechanisms, Raman spectroscopy, Sodium titanium silicate glasses, Structure-property relationships, Thermo-mechanical properties|
Copyright in each Dissertation and Thesis is retained by the author. All Rights Reserved
The supplemental file or files you are about to download were provided to ProQuest by the author as part of a
dissertation or thesis. The supplemental files are provided "AS IS" without warranty. ProQuest is not responsible for the
content, format or impact on the supplemental file(s) on our system. in some cases, the file type may be unknown or
may be a .exe file. We recommend caution as you open such files.
Copyright of the original materials contained in the supplemental file is retained by the author and your access to the
supplemental files is subject to the ProQuest Terms and Conditions of use.
Depending on the size of the file(s) you are downloading, the system may take some time to download them. Please be